SiC/SiC mini-composites with multilayer ZrSiO4 interphase: Room-temperature properties and toughening mechanism

SiC/SiC mini-composites reinforced with SiC fibers coated with different numbers of ZrSiO₄ sublayers prepared via a non-hydrolytic sol-gel process were fabricated. The tensile strength and work of fracture of the prepared SiC/SiC mini-composites were determined, and the relationship between their mechanical properties and fracture morphologies was discussed. The toughening mechanism and the variation tendency of their mechanical properties were further elaborated by analyzing the interfacial debonding morphologies of the SiC/SiC mini-composites with 1 and 4 layers of ZrSiO₄ interphase as well as the results of prior studies. A relatively rare phenomenon—the delamination of the multilayer ZrSiO₄ interphase in the SiC/SiC mini-composites but not on the SiC fibers—was observed, which clearly demonstrated the weak bonding between the ZrSiO₄ sublayers in the SiC/SiC mini-composites. The ZrSiO₄ sublayer delamination mechanism was then explained based on the high-magnification morphologies found in and beside the ZrSiO₄ interphase.     

Silica-based ceramics toward electromagnetic microwave absorption

Silica-based ceramics have been explored extensively as a class of versatile materials for various applications in architecture, catalysis, energy, machinery, and biomedical engineering. Nevertheless, comprehensive information on silica-based ceramic and electromagnetic microwave (EMW) absorption is scarce, although excellent progress has been made in this field. Here, recent progress in the investigation of silica-based ceramics toward EMW absorption is reviewed. We first introduced the basis of ceramics (characteristics, classification, synthetic methods, potential applications). Subsequently, the silica-based ceramics, including Si-based oxides and alloys, SiOC/SiC/Si₃N₄/SiCN-based composite, Ti₃SiC₂ and composite for EMW absorption were systematically summarized. Notably, the fabrication strategies, absorption properties, and mechanisms of silica-based ceramics are described in detail, with a focus on structure and component design. Lastly, the prospects and ongoing challenges of this field in the future are presented. This review is expected to learn from the past and achieve progress toward the future of silica-based ceramic for EMW absorption.     

Effect of Temperature and Strain Rate on the Hot Deformation Behaviour of Ferritic Stainless Steel

Metals and Materials International - The flow behaviour and microstructure characteristics of a ferritic stainless steel were investigated using plain strain compression test on a Gleeble 3500...     

Electrocatalytic activity of LaSr3Fe3O10 and LaSr3Fe3O10-GO towards oxygen reduction reaction in alkaline medium

Oxygen reduction reaction(ORR) plays a critical role in many energy conversion and storage processes.Therein, a comparative study of the electrocatalytic activity for ORR in 0.1 mol/L KOH solution was conducted using layered perovskite-like LaSr_3 Fe_3 O_(10) and LaSr3 Fe_3 O_(10)-graphene oxide(GO) composite as electrodes. Linear sweep voltammetry(LSV) results show that the LaSr3 Fe_3 O_(10)-GO hybrid exhibits higher current density, a more positive onset potential(-0.15 V vs. Hg/HgO) in comparison with LaSr_3 Fe_3 O_(10).The value of the overall transferred electrons for both catalysts implies a dominant two electron process for ORR. Both catalysts under alkalic conditions exhibit a two-step Tafel slope, suggesting a change in the reaction mechanism for ORR. The composite electrode exhibits a higher ORR current density, but inferior durability performances in relative to the LaSr_3 Fe_3 O_(10) electrode.     

改进的卷积神经网络单幅图像超分辨率重建

针对经典的基于卷积神经网络的单幅图像超分辨率重建方法网络较浅、提取的特征少、重建图像模糊等问题，提出了一种改进的卷积神经网络的单幅图像超分辨率重建方法，设计了由密集残差网络和反卷积网络组成的新型深度卷积神经网络结构。原始低分辨率图像输入网络，利用密集残差学习网络获取更丰富的有效特征并加快特征梯度流动，其次通过反卷积层将图像特征上采样到目标图像大小，再利用密集残差学习高维特征，最后融合不同卷积核提取的特征得到最终的重建图像。在Set5和Set14数据集上进行了实验，并和Bicubic、K-SVD、SelfEx、SRCNN等经典重建方法进行了对比，重建出的图像在整体清晰度和边缘锐度方面更好，另外峰值信噪比（PSNR）平均分别提高了2.69?dB、1.68?dB、0.74?dB和0.61?dB。实验结果表明，该方法能够获取更丰富的细节信息，得到更好的视觉效果，达到了图像超分辨率的增强任务。     

Effect of Molybdenum on the Microstructure and Oxidation Behavior of Hot-Pressed TaCr2 Alloys

Metal Science and Heat Treatment - Influence of molybdenum additions on the microstructure and corrosion resistance of powder alloys based on the TaCr2 Laves phase is studied. The phase composition...     

Grain growth kinetics and growth mechanism of columnar Al2O3 crystals in xNb2O5–7.5La2O3-Al2O3 ceramic composites

xNb₂O₅–7.5La₂O₃-Al₂O₃ ceramic composites with in-situ-grown columnar Al₂O₃ crystals were successfully prepared by microwave sintering at 1450–1525?°C using α-Al₂O₃, Nb₂O₅, and La₂O₃ powders as raw materials. X-ray diffraction results indicated that the main phases were Al₂O₃, LaNbO₄, and Nb₂O₅ in the prepared samples. A field emission scanning electron microscope (FESEM) showed that the Al₂O₃ crystals appeared as columnar in the structure. Moreover, the grain size of the columnar Al₂O₃ crystals increased with the Nb₂O₅ content. The ratio of the major axis to the minor axis of the crystals was largest when the Nb₂O₅ content was 15?vol%. Furthermore, the grain-growth kinetics index (n), growth activation energy (Q), and growth mechanism of the columnar Al₂O₃ crystals were studied. The results indicated that the Nb₂O₅ addition could promote formation and growth of columnar Al₂O₃ crystals, and the grain-growth activation energy indicated that the dissolution process controls the crystal growth. The growth mechanism of the columnar Al₂O₃ crystals was also studied. The present work demonstrated that Nb₂O₅ is a good additive for the preparation of Nb₂O₅–7.5La₂O₃-Al₂O₃ composite ceramics with columnar Al₂O₃ crystals.     

硅渣和玻璃粉直接烧结制备多孔材料的气孔结构与力学性能

以硅渣和玻璃粉为原料,采用粉体直接烧结法制备多孔材料,研究了烧结温度(700~900℃)、烧结时间(15~120min)和升温速率(10~100℃·min^-1)对多孔材料表观密度、气孔率、物相组成、抗压强度的影响。结果表明:气孔结构均匀性随烧结温度的升高而降低;表观密度随烧结温度的升高先减小后增大,随保温时间的延长而增大,随升温速率的增大而减小,气孔率的变化趋势与表观密度的相反;多孔材料的主要物相为玻璃相和硅、SiC、SiO2、Ca2Al2SiO7等结晶相,且结晶度随烧结温度的升高而降低;抗压强度随烧结温度的升高呈先增大后减小的趋势;当烧结温度为750℃,升温速率为30℃·min^-1,烧结时间为30 min时,多孔材料的主晶相为硅和Ca2Al2SiO7,抗压强度最大(1.60MPa),表观密度为0.43g·cm^-3,气孔率为80%。     

Facile preparation and strong adhesive strength of honeycomb polyurethane films with small pore diameter

With the continuous development of bionics, such as, geckos and virginia creeper with both superhydrophobic and super-adhesive, the surface wetting and super-adhesive properties of various porous materials have attracted extensive attention of the scientific and medical communities. Here, the honeycomb polyurethane (PU) porous films with strong adhesion were successfully prepared by microphase separation method and the effects of growth parameters on their microstructure and adhesive strength to ice were investigated. It was found that a high relative humidity (e.g., 100%) and a low solution concentration (e.g., 2%) facilitated the formation of ordered honeycomb PU porous films, and as-prepared PU pores with average pore diameter as small as 5 μm are better ordered and more uniform than these in related documents. Although the contact angle of water droplets on the surface of PU porous films increased from the premodification value of 85–130° to more than 160° after surface modification with polydopamine (PDA), the corresponding rolling angle remained approximately constant (180°), indicating that the surface of PU porous films has strong adhesion similar to geckos and virginia creeper. Furthermore, at lower temperature, the PU porous films exhibited the high adhesive strength of 142.13 kPa on ice, which was strongly dependent on the porous microstructures and surface compositions. The improved adhesive behavior to ice of honeycomb PU porous films modified with PDA provides new strategies for surface modification of materials and potential applications in medical domain.     

Low-temperature sintering of Al2O3 ceramics doped with 4CuO-TiO2-2Nb2O5 composite oxide sintering aid

Dense alumina ceramics doped with 5 wt% 4CuO-TiO₂-2Nb₂O₅ composite sintering aids were obtained at low sintering temperatures of 950∼975 °C. The ceramic sintered at optimal condition shows good microwave dielectric properties (ε_r = 12.7, Q × f = 7400 GHz), high thermal conductivity (18.4 W/m K) and high bending strength (320 MPa). TEM and EDS analysis revealed that amorphous Cu-Ti-Nb-O interfacial films with nanometer thickness formed at the grain boundaries, which could provide paths of mass transportation for densification. Al³⁺ ions may be involved in mass transportation through substitution by Ti³⁺ and Ti⁴⁺ ions near the grain boundary during the sintering process. The accumulation of copper ions at the trigeminal grain boundary was observed. The migration and reaction of copper ions in grain boundaries may also play an important role in promoting mass transportation and low-temperature densification of alumina ceramics.